Influence of Strain Rate on Properties of Microalloyed S-MC Steel Grades

E. Čižmárová
J. Micheľ
I. Mamuzić
M. Buršák

Puni tekst: engleski, pdf (452 KB) str. 285-290 preuzimanja: 210* citiraj
APA 6th Edition
Čižmárová, E., Micheľ, J., Mamuzić, I. i Buršák, M. (2002). Influence of Strain Rate on Properties of Microalloyed S-MC Steel Grades. Metalurgija, 41 (4), 285-290. Preuzeto s https://hrcak.srce.hr/128564
MLA 8th Edition
Čižmárová, E., et al. "Influence of Strain Rate on Properties of Microalloyed S-MC Steel Grades." Metalurgija, vol. 41, br. 4, 2002, str. 285-290. https://hrcak.srce.hr/128564. Citirano 24.08.2019.
Chicago 17th Edition
Čižmárová, E., J. Micheľ, I. Mamuzić i M. Buršák. "Influence of Strain Rate on Properties of Microalloyed S-MC Steel Grades." Metalurgija 41, br. 4 (2002): 285-290. https://hrcak.srce.hr/128564
Harvard
Čižmárová, E., et al. (2002). 'Influence of Strain Rate on Properties of Microalloyed S-MC Steel Grades', Metalurgija, 41(4), str. 285-290. Preuzeto s: https://hrcak.srce.hr/128564 (Datum pristupa: 24.08.2019.)
Vancouver
Čižmárová E, Micheľ J, Mamuzić I, Buršák M. Influence of Strain Rate on Properties of Microalloyed S-MC Steel Grades. Metalurgija [Internet]. 2002 [pristupljeno 24.08.2019.];41(4):285-290. Dostupno na: https://hrcak.srce.hr/128564
IEEE
E. Čižmárová, J. Micheľ, I. Mamuzić i M. Buršák, "Influence of Strain Rate on Properties of Microalloyed S-MC Steel Grades", Metalurgija, vol.41, br. 4, str. 285-290, 2002. [Online]. Dostupno na: https://hrcak.srce.hr/128564. [Citirano: 24.08.2019.]

Sažetak
The influence of strain rate on properties of microalloyed steel for cold drawing of S 315 MC and S 460 MC gra-des was analysed. It has been shown by testing these steel that strain rates in the range from 10-3 up to 1 s-1 do not influence the mechanical properties significantly. Significant strengthening started at strain rates exceeding 2 s-1. It has been shown also that the basic mechanical properties of the coldworked tested steel by 5 to 25 % were not influenced by prestrain at 10-3 to 103 s-1 strain rates. It is supposed according to the results, that the susceptibility to cold work of these steel was not influenced significantly by the strain rates usually used at coldwork (less than 1 s-1) and that the products after coldwork maintain their mechanical properties.