Drvna industrija, Vol. 66 No. 2, 2015.
Izvorni znanstveni članak
https://doi.org/10.5552/drind.2015.1356
Some Physical and Mechanical Properties of Borate-Treated Oriental Beech Wood
Hakan Simsek
; Sveučilište Gaziosmanpasa, Stručna visoka škola tehničkih znanosti u Tokatu, Odjel za znanost o drvu i drvnu tehnologiju, Tokat, Turska
Ergun Baysal
; Sveučilište Mugla Sitki Kocman, Tehnološki fakultet, Odjel za znanost o drvu i drvnu tehnologiju, Kotekli, Mugla, Turska
Sažetak
This study was designed to determine some physical properties such as surface roughness and oven dry density, and some mechanical properties such as modulus of elasticity (MOE) of borate-treated wood specimens. Wood specimens were prepared from Oriental beech (Fagus orientalis L.). Ammonium pentaborate octahydrate (APBO), ammonium tetrafluoroborate (ATFB), and sodium tetrafluoroborate (STFB) were used as borates. Before tests, wood specimens were impregnated with 0.25, 0.50, 1.50, and 3.00 percent aqueous solutions of borates. The results showed that borate treatment caused increases in oven dry density and surface roughness, while it decreased MOE values of Oriental beech. Generally, higher concentration levels of borates resulted in higher oven dry density and lower MOE of Oriental beech wood specimens.
Ključne riječi
borates; oven dry density; modulus of elasticity; surface roughness; Oriental beech