Utjecaj toplinske obrade na Charpy energiju udara mikrolegiranog čelika
Gorazd Kosec
; ACRONI d.o.o., C. B. Kidriča 44, 4270 Jesenice, Slovenia
Jelena Vojvodič Tuma
; Institute of Energetics, Mesarska 24, 1000 Ljubljana, Slovenia
Mirko Gojić
; University of Zagreb, Faculty of Metallurgy, Aleja narodnih heroja 3, 44103 Sisak, Croatia
Aleš Nagode
; University of Ljubljana, Faculty of Natural Sciences and Engineering, Aškerčeva c. 12, 1000 Ljubljana, Slovenia
Antun Stoić
; J. J. Strossmayer University of Osijek, Mechanical Engineering Faculty in Slavonski Brod, Trg Ivane Brlić Mažuranić 2, 35000 Slavonski Brod, Croatia
Ivan Samardžić
; J. J. Strossmayer University of Osijek, Mechanical Engineering Faculty in Slavonski Brod, Trg Ivane Brlić Mažuranić 2, 35000 Slavonski Brod, Croatia
Borut Kosec
; University of Ljubljana, Faculty of Natural Sciences and Engineering, Aškerčeva c. 12, 1000 Ljubljana, Slovenia
Sažetak
U ovom radu istraživan je niskolegirani visokočvrsti čelik Niomol 490K koji sadrži dodatak niobija (0,032 mas. %). Toplinska obrada čelika se sastojala od austenitizacije pri 1250 °C u trajanju od 5 minuta i ponovnog zagrijavanja do 750 °C u trajanju od 5 s. Nakon austenitizacije provedeno je kaljenje u vodi kod temperature od 70 °C i u olovnoj kupci do temperature od 400 °C uz naknadno hlađenje na zraku. Utvrđeno je da je Charpy energija udara viša, a prijelazna temperatura niža za transformaciju austenita u bainit nego kod transformacije austenita u martenzitnu mikrostrukturu. Eksperimentalni rezultati su pokazali različite prijelomne površine. Pokazano je da je preferentno cijepajući prijelom zapažen po ravnini rešetke (001), neovisno o mikrostrukturi.
Ključne riječi
Charpy energija udara; Prijelomna površina; HSLA čelik; Mikrostruktura; Prijelazna temperatura