Davor Bolf   ORCID icon orcid.org/0000-0001-5266-2194 ; University of Rijeka, Faculty of Engineering
Albert Zamarin   ORCID icon orcid.org/0000-0003-2691-5973 ; University of Rijeka, Faculty of Engineering
Robert Basan   ORCID icon orcid.org/0000-0002-3895-5051 ; University of Rijeka, Faculty of Engineering

Puni tekst: engleski, pdf (727 KB) str. 307-323 preuzimanja: 37* citiraj
APA 6th Edition
Bolf, D., Zamarin, A. i Basan, R. (2020). Composite Material Damage Processes . Pomorski zbornik, Special edition (3), 307-323. Preuzeto s https://hrcak.srce.hr/239020
MLA 8th Edition
Bolf, Davor, et al. "Composite Material Damage Processes ." Pomorski zbornik, vol. Special edition, br. 3, 2020, str. 307-323. https://hrcak.srce.hr/239020. Citirano 28.11.2020.
Chicago 17th Edition
Bolf, Davor, Albert Zamarin i Robert Basan. "Composite Material Damage Processes ." Pomorski zbornik Special edition, br. 3 (2020): 307-323. https://hrcak.srce.hr/239020
Harvard
Bolf, D., Zamarin, A., i Basan, R. (2020). 'Composite Material Damage Processes ', Pomorski zbornik, Special edition(3), str. 307-323. Preuzeto s: https://hrcak.srce.hr/239020 (Datum pristupa: 28.11.2020.)
Vancouver
Bolf D, Zamarin A, Basan R. Composite Material Damage Processes . Pomorski zbornik [Internet]. 2020 [pristupljeno 28.11.2020.];Special edition(3):307-323. Dostupno na: https://hrcak.srce.hr/239020
IEEE
D. Bolf, A. Zamarin i R. Basan, "Composite Material Damage Processes ", Pomorski zbornik, vol.Special edition, br. 3, str. 307-323, 2020. [Online]. Dostupno na: https://hrcak.srce.hr/239020. [Citirano: 28.11.2020.]

Sažetak
Composite materials are in use in the shipbuilding industry for a long period of time. Composites appear in vast number of fibre – matrix combinations and can be produced with several different production processes. Due to the specific nature of the composite material structure, the selection of the production process and the limitations in the quality control procedures, composite materials will always be subject to defects and imperfections which may, under certain circumstances, lead to the appearance and propagation of cracks. The size and the shape of the crack, the load type and the stress field in the material surrounding the crack will be crucial for crack growth and crack propagation. This paper reviews the composite material damage processes especially relevant for shipbuilding. The basic principles of composite material fracture mechanics are briefly explained, and finally, mechanisms responsible for the development of damage and fracture of composite materials are presented. This paper has emerged from the need to summarize information about composite material fracture and failure mechanisms and modes relevant for the shipbuilding industry.

Ključne riječi
composite material damage; composite material fracture; fracture mechanics; composites