Effect of acid-soluble aluminum content on precipitates and magnetic properties of grain oriented silicon steel

H. Y. Wang ; College of Applied Technology, University of Science and Technology Liaoning, Anshan, Liaoning, China
Y. Y. Shao ; College of Applied Technology, University of Science and Technology Liaoning, Anshan, Liaoning, China *
Z. W. Jia ; Iron and Steel Research Institutes , Ansteel Co. Ltd., Anshan, Liaoning, China
Q. Guo ; Cold Rolling Silicon Plant, Ansteel Co. Ltd., Anshan, Liaoning, China

* Dopisni autor.

Sažetak

The effect of acid-soluble aluminum content on precipitates and magnetic properties of grain oriented silicon steel was researched by optical microscopy and zeiss ultra 55 Scanning Electron Microscope (SEM) technique respectively. The results show that the number of precipitates increases with the increase of acid-soluble aluminum content, and the size of precipitates is relatively large after hot rolling. Under the low hot rolling temperature, the number of precipitates in the samples is large and the size is small, moreover, the grain size of the primary recrystallized grain is small. The matching of process parameters under different production process lines is the key to obtain good magnetic performance. The effect of nitriding on magnetic properties of the samples is related to the acidsoluble aluminum content of the samples. Too much acid-soluble aluminum can deteriorate the magnetic properties.

Ključne riječi

grain oriented silicon steel; acid-soluble aluminum; precipitates; magnetic properties