X-ray diffraction profile analysis of hexagonal cobalt in metastable compact powders
Anđelka M. Tonejc
; Department of Physics, Faculty of Science, P. 0. B. 162, 19, Marulićev trg, 41000 Zagreb, and Institute of Physics of the University Zagreb, Yugoslavia
Ankica Kirin
; Faculty of Medicine, 41000 Zagreb, Yugoslavia
Abstract
Samples of pressed cobalt powder were investigated using X-ray diffraction line profile analysis. Stacking fault parameters and microstrains were obtained using the single profile method and then compared with previous results., derived from the Warren-Averbach method. Both methods give comparable results for stacking fault paramaters and root mean square strains. The results obtained are of the same order of magnitude as those measured in plastically deformed cobalt.