Mehanička obrada laserom superlegure N-155 nakon dugotrajnog rada

Andjelka Milosavljevic ; University of Belgrade, Faculty of Mechanical Engineering, Kraljice Marije 16, 11020 Belgrade, Serbia
Sanja Petronic ; University of Belgrade, Faculty of Mechanical Engineering, Innovation Centre, Kraljice Marije 16, 11020 Belgrade, Serbia
Aleksander Kovacevic ; University of Belgrade, Institute of Physics, Pregrevica 118, 11080 Belgrade, Serbia
Zorica Kovacevic ; Institute for testing materials, Bulevar Vojvode Misica 43, 11000 Belgrade, Serbia
Zoran Stamenic ; University of Belgrade, Faculty of Mechanical Engineering, Kraljice Marije 16, 11020 Belgrade, Serbia

Sažetak

Uzorci superlegure željeza N-155 isječeni su iz lopatice turbine nakon dugotrajnog rada na povišenim temperaturama i tlakovima. Uzorci su izloženi impulsima lasera različitih parametara, promatrani skenirajućim elektronskim mikroskopom (SEM) i analizirani energodisperzivnom spektrometrijom (EDS). U ovisnosti o parametrima lasera, interakcija laserskog snopa i materijala je u nekim slučajevima promatrana kao mehanička, a u drugim kao termomehanička obrada. Mikrotvrdoće su mjerene po Vikersu. U ovom radu, analizirane su mikrostrukture nastale nakon različitih frekvencija impulsa i zatim uspoređene.

Ključne riječi

EDS; laser; mehanička obrada; mikrostruktura; SEM; superlegura