Metalurgija, Vol. 53 No. 4, 2014.
Izvorni znanstveni članak
Fatigue crack growth and fracture mechanics analysis of a working roll surface layer material
M. Drobne
; Valji, production of rolls and castings d.o.o., Slovenia
T. Vuherer
; University of Maribor, Faculty of Mechanical Engineering, Slovenia
I. Samardžić
; University of Osijek, Mechanical Engineering Faculty, Slavonski Brod, Croatia
S. Glodež
; University of Maribor, Faculty of Mechanical Engineering, Slovenia
Sažetak
Fatigue crack growth and fracture mechanics analysis of a working roll surface layer material is presented in this paper. The research is done on a hot strip mill working roll where High Chromium Steel is used for roll’s shell material. To obtain corresponding parameters, a rectangular single edge notched bend specimens – SENB, according to standard BS 7448, were used. The fatigue crack growth analysis was done on a resonant testing machine with use of special crack gauges, while for fracture mechanics parameters the electro–mechanical testing machine was used.
Ključne riječi
fracture mechanics; fatigue crack growth; rolling; high chromium steel