Međufazna sinteza FePO4 različitih morfologija i utjecaj morfologije na elektrokemijska svojstva LiFePO4/C

Y.-H. Luo ; School of Chemical Engineering; Nanjing University of Science and Technology Jiangsu, 210 094 Nanjing, Kina; National Quality Supervision and Inspection Center for Industrial Explosive Materials Jiangsu, 210 094 Nanjing, Kina
N. He ; Sinosteel Maanshan Institute of Mining Research Co., Ltd., Maanshan, 243 000 Anhui, Kina
Y.-C. Wang ; Sinosteel Anhui Tianyuan Technology Co., Ltd., 243 000 Anhui Maanshan, Kina
W.-G. Cao ; School of Chemical Engineering; Nanjing University of Science and Technology Jiangsu, 210 094 Nanjing, Kina
P. Feng ; School of Chemical Engineering; Nanjing University of Science and Technology Jiangsu, 210 094 Nanjing, Kina


Puni tekst: engleski pdf 1.192 Kb

str. 393-397

preuzimanja: 989

citiraj


Sažetak

U ovom je radu korištena metoda međufazne sinteze za pripravu FePO4 različitih morfologija te je istraživan učinak morfologije na pripravu i elektrokemijska svojstva LiFePO4/C. Rezultati su pokazali da je FePO4 pri temperaturi obrade 30 °C amorfan, a pri 80 °C monoklinski. LiFePO4/C je pripravljen iz dvaju prekursora oblika polukružne šupljine s kristalnom strukturom olivina. LiFePO4/C proizveden iz monoklinski strukturiranog prekursora pokazao je sitniju morfologiju i bolja elektrokemijska svojstva, a njegovi kapaciteti pražnjenja naboja bili su 155,9 mA h g–1 i 141,8 mA h g–1 pri brzini od 0.1 C i 1 C. Nakon 150 ciklusa, njegov kapacitet zadržavanja je oko 97,8 % i 95,1 % pri 0.1 C i 1 C

Ključne riječi

FePO<sub>4</sub>, LiFePO<sub>4</sub>/C; litij-ionska baterija; kompozitni materijali; energija pohrane i pretvorbe