Drvna industrija, Vol. 72 No. 1, 2021.
Izvorni znanstveni članak
https://doi.org/10.5552/drvind.2021.1913
Bending Characteristics of Laminated Wood Composites Made of Poplar Wood and GFRP
Mehmet Nuri Yildrim
orcid.org/0000-0002-0180-4479
; Karabuk University, Furniture Design and Decoration Department, Safranbolu Vocational School, Karabük, Turkey
Abdurrahman Karaman
orcid.org/0000-0002-5925-7519
; Usak University, Banaz Vocational School, Forestry Department, Usak, Turkey
Mustafa Zor
; Zonguldak Bulent Ecevit University, Caycuma Vocational School, Interior Design Programme, Zonguldak, Turkey
Sažetak
In this study, 4 layers of 5 mm thick slats obtained by sawing method from poplar wood were used. Plain woven GRFP with low density and grammage of 100 g/m2 (Type 1) and plain woven GRFP with high density and grammage of 200 g/m2 (Type 2) were placed and glued between each layer. Polyvinyl acetate (PVAc-D4), Polyurethane (PU) and dual-component Epoxy (L285-resin and H285-hardener) adhesives were used for gluing the layers. Strength values (bending and modulus of elasticity) between the obtained layers were investigated. As a result of the study, it was determined that epoxy glue has higher strength than polyurethane and polyvinyl acetate glues; Type 2 plain woven fabric has higher strength than Type 1 plain woven fabric; and parallel load to the glue line results in higher performance than perpendicular load to the glue line.
Ključne riječi
poplar; wood laminate; bending strength; modulus of elasticity