Skip to the main content

Original scientific paper

Influence of artillery weapon barrel superheat on abrasion wear resistance of material

Mirko Jakopčić ; Croatian Defence Academy "Petar Zrinski", Ilica 256 B, 10000 Zagreb, Croatia
Krešimir Grilec ; Faculty of Mechanical Engineering and Naval Architecture, University of Zagreb, Ivana Lučića 5, 10000 Zagreb, Croatia


Full text: croatian pdf 378 Kb

page 173-177

downloads: 420

cite

Full text: english pdf 378 Kb

page 173-177

downloads: 918

cite


Abstract

This paper studies the influence of the artillery weapon barrel superheat on abrasion wear resistance of material. The firing process has a compound mechanical, thermal and chemical effect on the barrel. Many wear mechanisms exist in the barrel in firing conditions: abrasion, adhesion, fatigue and tribocorrosion. This paper presents the procedure and the results of abrasion wear experiment. Some test samples were previously tempered and air cooled. The abrasion test samples were made of the heat treated steel 42CrMo4. Wear resistance is represented by the sample mass loss during the wear process. The test results show that unheated samples exhibit higher wear resistance in comparison with heated samples. A significant material wear increase of 43 % is shown in the samples which were heated at 900 °C. Conclusively, the test results show that excessive fire causes the weapon barrel to superheat and the material wear resistance to significantly decrease.

Keywords

abrasion wear; fire rate; superheat; weapon barrel