Utjecaj lantana na mikrostrukturu i svojstva čelika ASTM A216
Ai-Qin Wang
; School of Materials Science and Engineering, Henan University of Science and Technology, 471 023 Luoyang, P.R. China
Ming Li
; School of Materials Science and Engineering, Henan University of Science and Technology, 471 023 Luoyang, P.R. China
Douqin Ma
; School of Physical Engineering, Zhengzhou University, 450 001 Zhengzhou, Henan, P.R. China
Qinjie Wu
; School of Physical Engineering, Zhengzhou University, 450 001 Zhengzhou, Henan, P.R. China
Jingpei Xie
; School of Materials Science and Engineering, Henan University of Science and Technology, 471 023 Luoyang, P.R. China
Abstract
Da bi se zadovoljili standardi Međunarodnog udruženja klasifikacijskih zavoda (IACS) za lijevanje krmenog roga, potrebno je poboljšati svojstva čelika ASTM A216. Odljevci krmenog roda i prateći uzorci, nakon taljenja čelika u elektrolučnoj peći, rafiniranja i dodatka lantana, izrađeni su lijevanjem čelika u kalupe. Uzorci su prvo normalizirani zagrijavanjem 10 sati na 900 °C, ohlađeni na zraku, potom podvrgnuti popuštanju 7 sati na 600 °C i ponovno ohlađeni na zraku. Određena su mehanička svojstva uzoraka i proučena mikrostruktura. Analizirana je sličnost kristalne građe spojeva lantana nastalih u rastaljenom čeliku i δ-željeza. Izračunata je učinkovitost lantanovih spojeva kao podloge za heterogenu nukleaciju δ-željeza na temelju dvodimenzijskog nepodudaranja struktura. Dodatkom lantana vrpčasti uklopci MnS postaju zrnasti uklopci spoja rijetke zemlje. Finija mikrostruktura dobivena je sinergijskim djelovanjem povećane depresije kondenzata i brže
nukleacije uz lantan.
Keywords
čelik ASTM A216; uklopak; lantan; dvodimenzijsko nepodudaranje; profinjenje zrna