Characteristics of CuCrTiAl alloy after plastic deformation

M. Łagoda orcid.org/0000-0003-3679-6568 ; Łukasiewicz Research Network – Institute of Non-Ferrous Metals, Gliwice, Poland
W. Głuchowski ; Łukasiewicz Research Network – Institute of Non-Ferrous Metals, Gliwice, Poland
M. Maleta ; Łukasiewicz Research Network – Institute of Non-Ferrous Metals, Gliwice, Poland
J. Domagała-Dubiel ; Łukasiewicz Research Network – Institute of Non-Ferrous Metals, Gliwice, Poland
M. Sadzikowski orcid.org/0000-0002-9791-4137 ; AGH University of Science and Technology, Kraków, Poland

Abstract

The development of the automotive industry leads to the search for newer construction materials, but also those used in the production process. Although many types of joints are used in vehicles, resistance welds remain the dominant one. The commonly used alloy for welding caps (CuCrZr) is already well known and therefore newer alloys and technologies for their production are sought to increase service life, and thus reduce production costs. Precipitation hardening CuCrTiAl alloy was analysed in this article. After casting, CuCrTiAl alloy was subjected to cold and hot deformation and then tested for its usability. The obtained results confirmed the potential of this alloy to make electrodes for resistance welding.

Keywords

CuCrTiAl alloy; plastic deformation; precipitation hardening; microstructure; mechanical properties