Color Stability Assessment of Light and Self-Cured Composites Following Accelerated Aging
Samra Korać
orcid.org/0000-0001-7842-7299
; Katedra za restorativnu stomatologiju i endodonciju Stomatološkog fakulteta Sveučilišta u Sarajevu
Alma Đozić
; Odjel za ispitivanje dentalnih materijala Akademskog centra za stomatologiju, Amsterdam (ACTA), Nizozemska
Nedim Smajkić
; Katedra za restorativnu stomatologiju i endodonciju Stomatološkog fakulteta Sveučilišta u Sarajevu
Irmina Tahmiščija
; Katedra za restorativnu stomatologiju i endodonciju Stomatološkog fakulteta Sveučilišta u Sarajevu
Amra Vuković
orcid.org/0000-0001-9321-2253
; Katedra za pretkliničku stomatologiju Stomatološkog fakulteta Sveučilišta u Sarajevu
Selma Jakupović
; Katedra za restorativnu stomatologiju i endodonciju Stomatološkog fakulteta Sveučilišta u Sarajevu
Sažetak
Objectives: Measure and compare internal color stability of three light-cured composites and one chemically bonded material after their accelerated aging. Materials and Methods: Color stability tests included nano-filled Filtek Supreme XT (3M ESPE), nano-hybrid Tetric Evo Ceram (Ivoclar Vivadent), microhybrid Herculite XRV (Kerr) of light cured and Bisfil II (Bisco) of self cured composites. All samples were immersed in distilled water of 37°C and kept in a dark chamber during 24 hours. Thereafter they were divided into three groups. Accelerated aging was performed in accordance with the two different protocols, i.e. water bath at 60°C and ISO 7491. Control group specimens were stored in distilled water at 37°C for 30 days. Color differences, ΔE were calculated from CIE L*a*b* coordinates measured with spectrophotometer against white backing before and after aging of samples. The color perceptibility threshold was set at 1.7 and acceptability threshold at 3.5. Statistical tests carried out on the groups included paired t-test and ANOVA (p≤0.05). Results: All tested materials showed clinically unacceptable color changes after accelerated aging in water bath, whereas photoaging induced perceptible color change in all light-cured composites. Nano-engineered composites significantly changed their color also in the control group. Conclusions: Internal color stability of tested materials depends on aging conditions and type of dental composite. Chemically-cured material showed better color stability by photo aging.
Ključne riječi
Composite Resins; Aging; Materials Testing; Color