Effect of MgO content in sintered ore on viscosity of blast furnace slag bearing high Al₂O₃

F. Yang ; Wuhan University of Science and Technology, College of Resources and Environmental Engineering, Wuhan, China
Q. F. Qin ; Wuhan University of Science and Technology, College of Resources and Environmental Engineering, Wuhan, China
Y. Li ; Wuhan University of Science and Technology, College of Resources and Environmental Engineering, Wuhan, China
Y. Y. Huang ; Wuhan University of Science and Technology, College of Resources and Environmental Engineering, Wuhan, China
S. P. Wang ; Hebei Vocational University of industry and Technology, Shijiazhuang, China *

* Dopisni autor.

Sažetak

The effect of MgO content on the viscosity of blast furnace slag bearing high Al₂O₃ was studied under laboratory conditions. The viscosity of slag was determined by rotation method. The research results indicate that when the Al₂O₃ content in blast furnace slag is 17 % -18 %, the MgO content in blast furnace slag should be controlled at 10 %. When the Al₂O₃ content is 19 %, the MgO content should be controlled at 11 %, and the binary basicity of the slag should be controlled at around 1,10. This type of blast furnace slag has a lower melting point and better fluidity. The purpose of reducing the MgO content in the slag can be achieved by reducing the MgO content in sintered ore, that is, the MgO content in sintered ore should be controlled at 2,0 %-2,5 %.

Ključne riječi

blast furnace; the MgO content; sinter; slag bearing high Al₂O₃; viscosity