Weldability of microalloyed quenched and tempered steels as used in shipbuilding

Nedjeljko Mišina
Marijo Oršulić
Ivan Polajnar

Puni tekst: hrvatski, pdf (345 KB) str. 174-180 preuzimanja: 4.297* citiraj
APA 6th Edition
Mišina, N., Oršulić, M. i Polajnar, I. (2003). ZAVARLJIVOST MIKROLEGIRANIH POBOLJŠANIH ČELIKA RABLJENIH U BRODOGRADNJI. NAŠE MORE, 50 (5-6), 174-180. Preuzeto s https://hrcak.srce.hr/8566
MLA 8th Edition
Mišina, Nedjeljko, et al. "ZAVARLJIVOST MIKROLEGIRANIH POBOLJŠANIH ČELIKA RABLJENIH U BRODOGRADNJI." NAŠE MORE, vol. 50, br. 5-6, 2003, str. 174-180. https://hrcak.srce.hr/8566. Citirano 23.09.2021.
Chicago 17th Edition
Mišina, Nedjeljko, Marijo Oršulić i Ivan Polajnar. "ZAVARLJIVOST MIKROLEGIRANIH POBOLJŠANIH ČELIKA RABLJENIH U BRODOGRADNJI." NAŠE MORE 50, br. 5-6 (2003): 174-180. https://hrcak.srce.hr/8566
Harvard
Mišina, N., Oršulić, M., i Polajnar, I. (2003). 'ZAVARLJIVOST MIKROLEGIRANIH POBOLJŠANIH ČELIKA RABLJENIH U BRODOGRADNJI', NAŠE MORE, 50(5-6), str. 174-180. Preuzeto s: https://hrcak.srce.hr/8566 (Datum pristupa: 23.09.2021.)
Vancouver
Mišina N, Oršulić M, Polajnar I. ZAVARLJIVOST MIKROLEGIRANIH POBOLJŠANIH ČELIKA RABLJENIH U BRODOGRADNJI. NAŠE MORE [Internet]. 2003 [pristupljeno 23.09.2021.];50(5-6):174-180. Dostupno na: https://hrcak.srce.hr/8566
IEEE
N. Mišina, M. Oršulić i I. Polajnar, "ZAVARLJIVOST MIKROLEGIRANIH POBOLJŠANIH ČELIKA RABLJENIH U BRODOGRADNJI", NAŠE MORE, vol.50, br. 5-6, str. 174-180, 2003. [Online]. Dostupno na: https://hrcak.srce.hr/8566. [Citirano: 23.09.2021.]

Sažetak
This paper deals with the results of research conducted on quenched and tempered microalloyed steel. The welding process applied the MAG procedure with various heat inputs. In order to relieve the residual stresses, the annealing was done at 450, 550 and 650°C. The influence of heat input and stress relieving heat treatment has been researched by testing mechanical properties.

Hrčak ID: 8566