The Effect of Liquid Absorption on Gas Barrier Properties of Triplex Film Coated with Silicon Oxide

Kata Galić ; Faculty of Food Technology and Biotechnology, University of Zagreb, Pierottijeva 6, HR-10000 Zagreb, Croatia
Nada Ciković ; Faculty of Food Technology and Biotechnology, University of Zagreb, Pierottijeva 6, HR-10000 Zagreb, Croatia

Puni tekst: engleski, pdf (113 KB) str. 247-251 preuzimanja: 498* citiraj
APA 6th Edition
Galić, K. i Ciković, N. (2003). The Effect of Liquid Absorption on Gas Barrier Properties of Triplex Film Coated with Silicon Oxide. Food Technology and Biotechnology, 41 (3), 247-251. Preuzeto s https://hrcak.srce.hr/118634
MLA 8th Edition
Galić, Kata i Nada Ciković. "The Effect of Liquid Absorption on Gas Barrier Properties of Triplex Film Coated with Silicon Oxide." Food Technology and Biotechnology, vol. 41, br. 3, 2003, str. 247-251. https://hrcak.srce.hr/118634. Citirano 28.10.2021.
Chicago 17th Edition
Galić, Kata i Nada Ciković. "The Effect of Liquid Absorption on Gas Barrier Properties of Triplex Film Coated with Silicon Oxide." Food Technology and Biotechnology 41, br. 3 (2003): 247-251. https://hrcak.srce.hr/118634
Harvard
Galić, K., i Ciković, N. (2003). 'The Effect of Liquid Absorption on Gas Barrier Properties of Triplex Film Coated with Silicon Oxide', Food Technology and Biotechnology, 41(3), str. 247-251. Preuzeto s: https://hrcak.srce.hr/118634 (Datum pristupa: 28.10.2021.)
Vancouver
Galić K, Ciković N. The Effect of Liquid Absorption on Gas Barrier Properties of Triplex Film Coated with Silicon Oxide. Food Technology and Biotechnology [Internet]. 2003 [pristupljeno 28.10.2021.];41(3):247-251. Dostupno na: https://hrcak.srce.hr/118634
IEEE
K. Galić i N. Ciković, "The Effect of Liquid Absorption on Gas Barrier Properties of Triplex Film Coated with Silicon Oxide", Food Technology and Biotechnology, vol.41, br. 3, str. 247-251, 2003. [Online]. Dostupno na: https://hrcak.srce.hr/118634. [Citirano: 28.10.2021.]

Sažetak
Polymeric triplex film with SiOx deposit (polyethylene terephthalate/polyethylene terephthalate+ SiOx/polyethylene) was analysed for its gas permeance characteristics. For this purpose the permeance of triplex film to oxygen, nitrogen and carbon dioxide was
analysed before and after the immersion into the test solutions (ethanol, acetic acid and distilled water). Gas permeance measurements were performed in temperature range from
20 to 60 °C. The permeability of the treated triplex film (181–241 cm3m–2 d–1 bar–1) showed negligible changes in comparison with the untreated ones (164–257 cm3 m–2 d–1 bar–1). Due to the existence of inflection point at 40 oC, the Arrhenius equation was applied in narrow temperature ranges (20–35 oC and 40–60 oC). The obtained activation energies for the permeance of gases were correlated with different physical characteristics of permeates.

Ključne riječi
barrier properties; SiOx; temperature; test solutions; triplex film