Analysis and study test materials coke in a high temperature furnace

X. Y. Wang ; School of applied technology, University of Science and Technology Liaoning, Anshan, Liaoning, China
Y. Zeng ; General Ironmaking Plant of Angang Steel Co. Ltd, AnShan, Liaoning, China

Puni tekst: engleski, pdf (714 KB) str. 537-539 preuzimanja: 26* citiraj
APA 6th Edition
Wang, X.Y. i Zeng, Y. (2020). Analysis and study test materials coke in a high temperature furnace. Metalurgija, 59 (4), 537-539. Preuzeto s https://hrcak.srce.hr/241212
MLA 8th Edition
Wang, X. Y. i Y. Zeng. "Analysis and study test materials coke in a high temperature furnace." Metalurgija, vol. 59, br. 4, 2020, str. 537-539. https://hrcak.srce.hr/241212. Citirano 22.10.2020.
Chicago 17th Edition
Wang, X. Y. i Y. Zeng. "Analysis and study test materials coke in a high temperature furnace." Metalurgija 59, br. 4 (2020): 537-539. https://hrcak.srce.hr/241212
Harvard
Wang, X.Y., i Zeng, Y. (2020). 'Analysis and study test materials coke in a high temperature furnace', Metalurgija, 59(4), str. 537-539. Preuzeto s: https://hrcak.srce.hr/241212 (Datum pristupa: 22.10.2020.)
Vancouver
Wang XY, Zeng Y. Analysis and study test materials coke in a high temperature furnace. Metalurgija [Internet]. 2020 [pristupljeno 22.10.2020.];59(4):537-539. Dostupno na: https://hrcak.srce.hr/241212
IEEE
X.Y. Wang i Y. Zeng, "Analysis and study test materials coke in a high temperature furnace", Metalurgija, vol.59, br. 4, str. 537-539, 2020. [Online]. Dostupno na: https://hrcak.srce.hr/241212. [Citirano: 22.10.2020.]

Sažetak
The test material of a high temperature furnace is coke. in order to study the influence of temperature on the reactivity of coke, the reactivity index and weight loss rate of coke were measured under different reaction temperature conditions, and the dynamic observation of coke reaction process was made under the microscope. The reaction mechanism of coke was analyzed, and the influence of temperature on metallurgical properties was evaluated.

Ključne riječi
coke temperature; reactivity index; weight loss ratio; metallurgical properties