Izvorni znanstveni članak

Carboxylated Polyurethanes Containing Hyperbranched Polyester Soft Segments

G. Prevec
E. Žagar
M. Žigon

Sažetak

hyperbranched polyester soft segments (HB PU) with functional carboxylic groups in order to enable the preparation of stable HB PU dispersions. Carboxylated hyperbranched polyurethanes were synthesized using a hyperbranched polyester based on 2,2-bis(methylol)propionic acid of the fourth pseudo-generation (BoltornŽ H40) and hexamethylene (HDI) or isophorone diisocyanate (IPDI). The reactivity of hyperbranched polyester with HDI was lower than expected, possibly due to the presence of less reactive hydroxyl groups in the linear repeat units. A gel was formed at mole ratios r_NCO/OH = 1:2 or 1:4. The synthesis of HB PU was performed with partly esterified hyperbranched polyester with lowered hydroxyl functionality. The carboxyl groups were incorporated in the HB PU backbone by reaction of residual hydroxyl groups with cis-1,2-cyclohexanedicarboxylic anhydride. HB PU aqueous dispersions were stable at least for two months, although their films were brittle. The tensile strength and Young's modulus of blends of linear and HB PU decreased with increasing content of HB PU whereas elongation at break remained nearly constant, which was explained in terms of looser chain packing due to more open tree-like hyperbranched structures.

Ključne riječi

polyurethanes: polyurethane anionomers; hyperbranched polymers; aqueous dispersions

Hrčak ID:

6696

URI

https://hrcak.srce.hr/6696

Datum izdavanja:

11.9.2006.

Podaci na drugim jezicima: hrvatski

Posjeta: 1.862 *