Utjecaj toplinske obrade na mikrostrukturu i mehanička svojstva legure Cu-Al-Mn s prisjetljivosti oblika

Stjepan Kožuh ; University of Zagreb, Faculty of Metallurgy, Aleja narodnih heroja 3, 44 103 Sisak, Croatia
Mirko Gojić ; University of Zagreb, Faculty of Metallurgy, Aleja narodnih heroja 3, 44 103 Sisak, Croatia
Ivana Ivanić ; University of Zagreb, Faculty of Metallurgy, Aleja narodnih heroja 3, 44 103 Sisak, Croatia
Tamara Holjevac Grgurić ; University of Zagreb, Faculty of Metallurgy, Aleja narodnih heroja 3, 44 103 Sisak, Croatia
Borut Kosec ; University of Ljubljana, Faculty of Natural Science and Engineering, Aškerčeva 12, 1000, Ljubljana, Slovenia
Ivan Anžel ; University of Maribor, Faculty of Mechanical Engineering, Smetanova 17, 2000, Maribor, Slovenia

Abstract

Šipke promjera 8 mm proizvedene su iz legure Cu-Al-Mn s prisjetljivosti oblika tehnikom kontinuiranog lijevanja. Uzorci su karakterizirani pomoću optičke mikroskopije i pretražne elektronske mikroskopije uz analizu EDX. Kontinuirano lijevana legura je pokazala mjestimičnu prisutnost martenzitne faze, dok je nakon kaljenja nastala potpuno martenzitna mikrostruktura. Kaljenje uzoraka utjecalo je na mehanička svojstva i na promjenu morfologije prijeloma. Nakon starenja pri 200 °C i 300 °C porasla je vlačna čvrstoća a izduženje se drastično smanjilo. Morfologija prijelomne površine se mijenjala od duktilne do mješavine interkristalne i duktilne.


Ovo djelo je dano na korištenje pod licencom Creative Commons Imenovanje 4.0 međunarodna.

Keywords

legure s prisjetljivosti oblika (SMAs); mehanička svojstva; mikrostruktura; pretražna elektronska mikroskopija (SEM); kaljenje; starenje