Research on Cu-Mg castings cold drawing process and analysis of mechanical and electrical properties of obtained wires

G. Kiesiewicz orcid.org/0000-0001-9518-5498 ; AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Cracow, Poland
P. Kwasniewski orcid.org/0000-0002-7826-6672 ; AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Cracow, Poland
W. Sciezor orcid.org/0000-0001-8974-5970 ; AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Cracow, Poland
K. Franczak orcid.org/0000-0002-0135-3700 ; AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Cracow, Poland
M. Sadzikowski orcid.org/0000-0002-9791-4137 ; AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Cracow, Poland
S. Kordaszewski orcid.org/0000-0002-5455-2025 ; AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Cracow, Poland

Abstract

The aim of the conducted research works which are presented in the article was to determine the mechanical and electrical properties of Cu-Mg wires obtained in cold drawing process with total deformation at the level of 95 %. Base material for the research was obtained with the use of continuous casting process which allowed to produce CuMg0.02, CuMg0.05 and CuMg0.5 cylindrical rods with 9,5 mm diameter which were next cold drawn up to 1,97 mm diameter. After the cold drawing process Vickers hardness measurements along with static tensile test and electrical conductivity analysis were performed in order to determine the evolution of castings properties as a result of the applied cold deformation.

Keywords

cold drawing; wire; Cu-Mg alloys; mechanical properties; electrical conductivity