Carbon nitride-assisted thermal treatment for sintering-resistant Pt/C catalysts
Junyi Li
; School of Materials Science and Engineering, Peking University, Beijing 100871, China
Liang Tian
; Instituto de Tecnología Química, Consejo Superior de Investigaciones Científicas-Universitat Politècnica de Valencia, Universitat Politècnica de Valencia, Av. De los Naranjos s/n, 46022 Valencia, Spain
*
Ying Wang
; State Key Laboratory of Green Papermaking and Resource Recycling, Qilu University of Technology (Shandong Academy of Sciences), Jinan 250353, China
* Dopisni autor.
Sažetak
High-temperature annealing often induces severe sintering of Pt nanoparticles in Pt/C catalysts, resulting in activity degradation. Here, a carbon nitride–assisted thermal treatment strategy is proposed to enhance the thermal stability of Pt/C. TG-FTIR and XPS analysis reveal that nitrogen-containing species generated during carbon nitride decomposition play a key role in suppressing Pt nanoparticle coalescence at intermediate temperatures. Although the carbon nitride framework decomposes at high temperatures, residual graphitic and pyridinic nitrogen species are retained and interact electronically with Pt, leading to a reduced Pt binding energy. As a result, the carbon nitride–assisted Pt/C maintains a narrow particle size distribution after annealing. Electrochemical measurements demonstrate that the assisted catalyst retains oxygen reduction reaction activity comparable to commercial Pt/C after thermal treatment at 700 °C, while the untreated sample shows pronounced performance loss. Moreover, the assisted catalyst exhibits significantly improved durability after 20 000 cycles. This work offers a simple and effective approach to improving the thermal robustness of Pt-based electrocatalysts for PEM fuel cells.
Ključne riječi
Carbon nitride decomposition; platinum nanoparticles; sintering suppression; oxygen reduction reaction; electrochemical durability