Impact of the heat treatment parameters on ultimate tensile strength, microstructure and wire drawing process of Zn-Al15

P. Strzępek ; AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Cracow, Poland
P. Osuch ; AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Cracow, Poland
M. Walkowicz ; AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Cracow, Poland
M. Zasadzińska ; AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Cracow, Poland
A. Mamala ; AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Cracow, Poland
T. Knych ; AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Cracow, Poland
T. Napióra ; ZM Silesia S.A., Katowice, Poland

Puni tekst: engleski, pdf (2 MB) str. 489-492 preuzimanja: 48* citiraj
APA 6th Edition
Strzępek, P., Osuch, P., Walkowicz, M., Zasadzińska, M., Mamala, A., Knych, T. i Napióra, T. (2020). Impact of the heat treatment parameters on ultimate tensile strength, microstructure and wire drawing process of Zn-Al15. Metalurgija, 59 (4), 489-492. Preuzeto s https://hrcak.srce.hr/241167
MLA 8th Edition
Strzępek, P., et al. "Impact of the heat treatment parameters on ultimate tensile strength, microstructure and wire drawing process of Zn-Al15." Metalurgija, vol. 59, br. 4, 2020, str. 489-492. https://hrcak.srce.hr/241167. Citirano 20.10.2020.
Chicago 17th Edition
Strzępek, P., P. Osuch, M. Walkowicz, M. Zasadzińska, A. Mamala, T. Knych i T. Napióra. "Impact of the heat treatment parameters on ultimate tensile strength, microstructure and wire drawing process of Zn-Al15." Metalurgija 59, br. 4 (2020): 489-492. https://hrcak.srce.hr/241167
Harvard
Strzępek, P., et al. (2020). 'Impact of the heat treatment parameters on ultimate tensile strength, microstructure and wire drawing process of Zn-Al15', Metalurgija, 59(4), str. 489-492. Preuzeto s: https://hrcak.srce.hr/241167 (Datum pristupa: 20.10.2020.)
Vancouver
Strzępek P, Osuch P, Walkowicz M, Zasadzińska M, Mamala A, Knych T i sur. Impact of the heat treatment parameters on ultimate tensile strength, microstructure and wire drawing process of Zn-Al15. Metalurgija [Internet]. 2020 [pristupljeno 20.10.2020.];59(4):489-492. Dostupno na: https://hrcak.srce.hr/241167
IEEE
P. Strzępek, et al., "Impact of the heat treatment parameters on ultimate tensile strength, microstructure and wire drawing process of Zn-Al15", Metalurgija, vol.59, br. 4, str. 489-492, 2020. [Online]. Dostupno na: https://hrcak.srce.hr/241167. [Citirano: 20.10.2020.]

Sažetak
Research conducted in the current paper examines the impact of the heat treatment at temperatures from 150 °C to 300 °C with time intervals between 1 and 6 hours on susceptibility to drawing process of Zn-Al15 wire rod manufactured within the industrial continuous casting and rolling line. The mechanical properties studies proved that the heat treatment caused the increase in the ultimate tensile strength values of the alloy whereas the drawing process caused a significant decrease, which suggests that this alloy after the specific heat treatment cannot be subjected to strain hardening.

Ključne riječi
Zn-Al15 alloy; wire drawing; heat treatment; microstructure; mechanical properties